Feature(may vary by option.)

●Thick putty with special polishing properties, non-shrinkable, ultra-lightweight putty
●It has strong adhesion to ultra high tensile steel sheets, aluminum sheets, general steel sheets, iron sheets, wood, and other FRP applications, with strong edges. Heat resistant for about 30 minutes at 150 to 180 degrees Celsius and has a high heat resistance, so you can safely dry it or burn it after coating (heat resistant temperature varies depending on film thickness and weather conditions)
●Dries well and does not leave surface tacks. Furthermore, by forced drying (5-10 minutes at 50-60 degrees Celsius), polishing time can be significantly reduced. It has excellent low shrinkability that is good to say no shrinkage, so the steel sheet can be firmly bounded without warping after hardening, preventing the occurrence of sledding, distortion, and shrinkage. After curing, the putty is flexible and conformable for a certain time, and the putty absorbs distortion. It has excellent blister resistance and does not have surface tacks unique to non-shrink putty, so the paper can be firmly bite and polished. Be careful not to over-sharpen. You can also mix and match the main ingredient of Legend.I, so you can adjust the viscosity to your preference
●Contents: Main agent: 4.9 lbs (2.2 kg); Hardener: 2.8 oz (80 g); Color: Main agent: Light purple, Hardener: Yellow
●[Non-return] For chemical industry, we cannot accept returns except for product defects

[Hardener C Brown Set]

[Main agent only | no hardener]

[Hardener C Clear Set]

[Hardener C Yellow Set]

Description

[Features] 1. Adhesion: Super high tensile steel sheets, high tensile steel sheets, rust proof steel sheets, aluminum sheets, general steel sheets, and other FRP parts are very strong.
2. Heat resistance: Heat resistant for about 30 minutes at 150 to 180 degrees Celsius, and the heat resistance temperature is high, so you can bake it after coating with peace of mind (heat resistant temperature varies depending on conditions such as thickness of membrane).
3. Drying: Dramatically improves dryness and leaves no surface tack Furthermore, by forced drying (5-10 minutes at 50-60 degrees Celsius), polishing time can be significantly reduced.
4. Moisture Resistance: Superior blister resistance.
5. Shrinkage: With excellent non-shrinkage properties, the steel sheet can be firmly bounded without distortion after hardening, and it reduces the occurrence of snagging, distortion, and shrinkage.
6. Flexibility: After curing, the putty is flexible and conforming to the putty, and the putty absorbs distortion.
7. Polishing: There is no surface tack that is unique to non-shrink putty, so the paper sticks firmly without tangling the paper and does not slip on the surface, making it crisp. Instead of the crunchy surface with a semi-dry surface, it can be easily sanded with a light and crisp texture of paper while completely dry.
8. Type: S (summer), N (standard = spring and autumn), W (winter).
9. Other: Main agent mixing system blending is OK.
Hardener C Yellow 2.8 oz (80 g)